Cathode collector bar for Aluminum melting plant
SAE 1006 Cathode bar is used for electrolytic aluminium factory, the low carbon steel has good electrical conductivity. Our product is produced in big steel factory, the quality is very good, we can supply any size products as your requirement, please contact us to talk about the details.
1 Order contents
Contracts or orders placed under this standard should include the following:
Special technical requirements (such as guide processing, etc.)
The following definitions apply to this standard.
2 brand representation
Flat steel grades are indicated by steel grades and cross-section dimensions, such as Q215-120×198. Q195 - carbon structural steel grade, 120 × 198 - the sectional size of the cathode flat steel.
3 Size, shape, weight and allowable deviation
3.1 The flat steel thickness and its allowable deviation shall comply with the requirements of Table 1.
Table 1 Thickness tolerance mm
3.2 The width of the flat steel and its allowable deviation shall comply with the provisions of Table 2.
Table 2 width tolerance mm
3.3 Flat steel length and its allowable deviation
The cathode flat steel is delivered according to a fixed length, the length of the fixed length shall be specified in the contract, and its allowable length deviation is 0 to +15 mm.
3.4 The bending of the length of the cathode flat bar shall comply with the requirements of Table 3.
Table 3 Curvature mm
Degree of roughness
3.5 The four corners along the length of flat steel, the arc radius 5mm ~ 15mm.
3.6 After consultation between the supplier and the buyer, special specifications and requirements are ordered according to the agreement between the supplier and the buyer.
Cathode flat steel is delivered according to actual weight. After negotiations between supply and demand sides, they can also be delivered according to theoretical weight. Flat steel measurements are calculated according to nominal dimensions and the specific gravity is calculated at 7.85t/m3.
4 Technical Requirements
4.1 Chemical composition
4.1.1 The chemical composition of the flat steel (smelting analysis) shall comply with the provisions of Table 6.
4.1.2 After negotiations between the supplier and the buyer, other brands than GB/T 700 may also be used, and they must be specified in the contract.
The allowable deviation of the finished chemical composition of the flat steel shall comply with the provisions of GB/T 222.
Table 3 Chemical composition of flat steel
4.2 Mechanical properties
The mechanical properties do not serve as delivery conditions for the cathode flat steel.
4.3 Method of manufacture
Flat steel raw material is smelted by Oxygen converter of 40T or more
4.3.2 Roll Forming
It is rolled into rectangular strip or thick steel plate by hot rolling and then processed into rectangular flat steel according to the required size by sawing or flame cutting.
4.4 Surface quality
The surface of the flat steel must not have visible cracks, folds, scabs, inclusions, and pressed iron oxide skin. If the above defects must be removed along the length direction, the clearance depth shall be calculated from the actual size of the flat steel and shall not exceed half of the tolerance.
4.5 Internal quality
Flat steel cross-section after acid immersion low magnification test, the organization is uniform, there must be visible to the naked eye shrinkage, bubbles, cracks and other defects.
5 Test methods
The inspection items and test methods for each batch of steel shall comply with the requirements in Table 5.
Chemical composition (smelting analysis)
GB/T 223,GB/T 4336
|GB/T 2975||GB/T 228.1|
|Surface||One by one||/||Visual inspection|
|Dimensions Branch||One by one||/|
Caliper, Steel Tape Measure
6 Inspection Rules
6.1 Inspection and Acceptance
The inspection and acceptance of flat steel products are carried out by the supplier's quality and technical supervision department.
6.2 Group Batch Rules
Flat steel shall be inspected and accepted in batches. Each batch consists of the same brand and the same size as the furnace.
6.3 Sample size and sampling location
The sampling quantity and sampling location of each batch of steel shall comply with the requirements of Table 5.
6.4 Review and Decision Rules
Flat steel re-inspection and determination rules according to GB/T 17505 regulations.
7 Packaging, Signs, and Quality Certificates
7.1 Flat steel must be delivered in bales. The weight of each bale is determined by the parties to the supply and demand.
7.2 Three bundles shall be bundled for each full length of bundle and shall be firm, fastened, and flush at both ends.
7.3 The flat steel mark and quality certificate shall meet the relevant requirements of GB/T 2101.