گیلی ری سائیکلنگ ٹیکنالوجی کا استعمال کرتے ہوئے فضلہ لیتھیم آئن بیٹریوں کے علاج کا طریقہ

فضلہ لیتھیم آئن بیٹریوں کے علاج کے لیے گیلی ری سائیکلنگ ٹیکنالوجی کو اپنانا اور ایلومینیم کی بازیافت کے لیے عمل کی شرائط, کوبالٹ, اور لتیم دھاتی عناصر. پر 90 ℃, leaching aluminum with 10% NaOH resulted in a leaching rate of 96%. Under the leaching conditions of 90 ℃ and 4 mol/L H2SO4 solution, with a solid-liquid ratio of 1:8 and a reaction time of 100 minutes, the leaching rates of cobalt and lithium were 92%, respectively. By using NaHCO3 and Na2CO3 as precipitants, CoCO3 and Li2CO3 products can be prepared from acidic leaching solution, respectively.
The specific operation steps are as follows:
1. Waste battery pre-treatment: سب سے پہلے, it is necessary to pre-treat the waste battery, including removing the shell and packaging materials. This can be done through mechanical processing or physical methods.
2. Filter solid impurities: Filter the pretreated waste battery material to remove solid impurities such as metal residues, plastics, وغیرہ.
3. Lithium aluminum separation: Under appropriate conditions, use alkaline solution (such as 10% NaOH) for leaching to extract aluminum from waste batteries. پر 90 ℃, the leaching rate of aluminum can reach 96%. پھر, aluminum can be precipitated out through precipitation or other methods to obtain high-purity aluminum products.
4. Cobalt lithium recovery: For the remaining leaching solution, sulfuric acid (H2SO4) is usually used for leaching at appropriate temperature, concentration, solid-liquid ratio, and reaction time. Under the process conditions of a temperature of 90 ℃, a concentration of 4 mol/L of H2SO4 solution, a solid-liquid ratio of 1:8, and a reaction time of 100 minutes, the leaching rate of cobalt and lithium can reach 92%. پھر, by adding NaHCO3 and Na2CO3 as precipitants, cobalt and lithium were converted into CoCO3 and Li2CO3 precipitates, respectively.
5. Sediment treatment: آخر میں, further treat the obtained CoCO3 and Li2CO3 precipitates. High purity cobalt and lithium products can usually be extracted through process steps such as filtration, washing, and drying.
خلاصہ, wet recovery technology is an effective method for treating waste lithium-ion batteries and recovering aluminum, کوبالٹ, and lithium metal elements from them. This technology helps to reduce the environmental pollution caused by discarded batteries, and can recycle and reuse valuable metal resources within them.

ہم R پر توجہ مرکوز کرنے کے لیے خصوصی ہیں۔&ڈی دھات نکالنے والے ری ایجنٹس, ذیل کے طور پر ہماری اہم مصنوعات:

1. DZ988N/DZ973N/ڈی زیڈ 902 تانبے سالوینٹس نکالنے والا ری ایجنٹ.
2. DY319 اعلی کارکردگی نکل کوبالٹ شریک نکالنے والا نکالنے والا, نکل لیٹریٹ ایسک یا لیتھیم بیٹری الیکٹرولائٹ سے نکل اور کوبالٹ ایک ساتھ نکال سکتے ہیں.
3. DZ272 نکل کوبالٹ علیحدگی نکالنے والا, یہ نکل کوبالٹ محلول سے کوبالٹ نکال سکتا ہے۔.
4. DY377 موثر نکل اور ہیرے کو الگ کرنے والا نکالنے والا.
5. DY366 نیا جدید نکل کوبالٹ نکالنے والا.
6. ص204 (D2EHPA یا HDEHP) نکالنے والا.
7. DY301, جوہری خرچ شدہ ایندھن کی وصولی کے لیے DY302.
8. وینیڈیم ایکسٹریکٹنٹ کے لیے دیگر نکالنے والے ری ایجنٹس, لتیم نکالنے والا, فیرو نکالنے والا اور نایاب زمین نکالنے والا.