روش تولید پیش ساز (Ni1/3Co1/3Mn1/3) 3O4 برای مواد الکترود مثبت نیکل کبالت منگنز لیتیوم

The production method for the precursor (Ni1/3Co1/3Mn1/3) 3O4 of nickel cobalt manganese lithium positive electrode material involves several key steps.

اولا, the preparation of nickel cobalt manganese alloy powder is conducted by combining metal nickel, کبالت, و منگنز به نسبت مولی 1:1:1. Under nitrogen protection, the mixture is heated and melted. The molten metal liquid is then atomized using high-pressure nitrogen gas flow, منجر به تشکیل پودر آلیاژ نیکل کبالت منگنز می شود. These particles exhibit a regular spherical shape with a loose density of 5.1 g/cm3 و چگالی متراکم شده از 5.6 g/cm3. The high-temperature melting process allows for the uniform mixing of nickel, کبالت, and manganese at the atomic level, promoting the subsequent production of highly homogeneous nickel cobalt manganese oxides.

The next step involves oxidizing the nickel cobalt manganese alloy powder to obtain nickel cobalt manganese oxide. The alloy powder is placed inside an oxidation furnace equipped with stirring and ventilation. By introducing compressed air at a pressure of 0.7 MPa and maintaining dynamic conditions, the material undergoes roasting and oxidation. فرآیند اکسیداسیون در دمایی از 900 ℃ برای مدت زمان 3 ساعت ها. Afterward, the oxidized product is transferred to an airflow mill for crushing treatment. This step requires an air consumption of 1.5 m3/min at an air pressure of 0.8 MPa. نیکل کبالت اکسید منگنز حاصل (Ni1/3Co1/3Mn1/3) 3O4 exhibits an average particle size (D50) از 15 میکرومتر. It possesses a loose density of 2.1 g/cm3 و چگالی متراکم شده از 2.7 g/cm3. The oxide structure of the nickel cobalt manganese oxide is well-formed, and the particles exhibit a uniform spherical shape.

به طور خلاصه, the production method for the precursor (Ni1/3Co1/3Mn1/3) 3O4 involves the preparation of nickel cobalt manganese alloy powder through melting and atomization processes. متعاقبا, the alloy powder is oxidized at high temperature, resulting in the formation of nickel cobalt manganese oxide. This method ensures the production of highly homogeneous oxide particles with favorable characteristics for their application as positive electrode materials in nickel cobalt manganese lithium batteries.

If you need the related nickel cobalt copper extractants, لطفا از ما بپرسید:

استخراج کننده های فلزی ما به شرح زیر است:

1. DZ988N/DZ973N/DZ902 معرف استخراج با حلال مس.
2. DY319 استخراج کننده نیکل کبالت با راندمان بالا, می تواند نیکل و کبالت را با هم از سنگ معدن نیکل لاتریت یا الکترولیت باتری لیتیوم خارج کند.
3. DZ272 استخراج کننده نیکل کبالت, می تواند کبالت را از محلول نیکل کبالت خارج کند.
4. DY377 استخراج کننده کارآمد جداسازی نیکل و الماس.
5. DY366 استخراج کننده کبالت نیکل پیشرفته جدید.
6. P204 (D2EHPA یا HDEHP) استخراج کننده.
7. DY301, DY302 برای بازیابی سوخت مصرف شده هسته ای.
8. سایر معرف های استخراج برای استخراج کننده وانادیوم, استخراج کننده لیتیوم, استخراج کننده فرو و استخراج خاکی کمیاب.